41. A retest shall be permitted for two random specimen if these fall (a) within 14 MPa of the required yield strength (b) within 7 MPa of the required tensile strength (c) within 7% unit of the required bending strength (d) within 2% unit of the required elongation 42. It is commonly known as synthetic amalgamated material made up of plastic and extremely fine fibers. It is the largest segment in the composite industry. (a) Aramid FRP (c) Carbon FRP (b) Basalt FRP (d) Glass FRP 43. It is a silver-colored metal that conducts heat and electricity well. It only occurs naturally in the Earth's crust as ores, such as hematite, magnetite, and siderite. One of its identifying characteristics is that it is strongly magnetic. (c) Pure Iron (d) Quenched Tempered Alloy Steel (a) Carbon Steel (b) High Strength Steel

41. A retest shall be permitted for two random specimen if these fall (a) within 14 MPa of the required yield strength (b) within 7 MPa of the required tensile strength (c) within 7% unit of the required bending strength (d) within 2% unit of the required elongation 42. It is commonly known as synthetic amalgamated material made up of plastic and extremely fine fibers. It is the largest segment in the composite industry. (a) Aramid FRP (c) Carbon FRP (b) Basalt FRP (d) Glass FRP 43. It is a silver-colored metal that conducts heat and electricity well. It only occurs naturally in the Earth's crust as ores, such as hematite, magnetite, and siderite. One of its identifying characteristics is that it is strongly magnetic. (c) Pure Iron (d) Quenched Tempered Alloy Steel (a) Carbon Steel (b) High Strength Steel

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.1P

See similar textbooks

Similar questions

A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
The frame of a space shuttle type vehicle must have a high yield strength and high stillness, and the most important design factor is weight. Of all the materials presented in this chapter, what material might be the most suitable for the frame of a space shuttle? Assume that there will be both tensile and compressive stresses. For a space shuttle, cost is not a limiting factor. (a) You can eliminate entire classes of materials from consideration with a brief statement about their unsuitability. (b) What material has the highest specific yield strength? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (c) What material has the highest specific elastic modulus? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (d) Compare the materials with the highest specific yield strength and highest specific elastic modulus for suitability in the space shuttle frame. (C) Discuss the suitability of the top-rated material for this design from the viewpoint of the ability to produce a frame.
(b) (i) A tensile test specimen made from 0.4% C steel has a circular cross section of diameter d mm and a gauge length of 25 mm. When a load of 4500 N is applied during the test, the gauge length of the specimen extends to 25.02 mm. If the Young's Modulus of the steel is 199 GPa, calculate the diameter of the tensile test specimen used. 4
A steel bar and an aluminum bar are bonded together as shown to form a composite beam. Knowing that the vertical shear in the beam is 4 kips and that the modulus of elasticity is 29 * 106 psi for the steel and 10.6 *106 psi for the aluminum, determine (a) the aver-age shearing stress at the bonded surface, (b) the maximum shearing stress in the beam.
During a tensile test on a specimen of steel the following data was recorded diameter of the specimen is 6.6mm,gage length 5mm,elongation of a load of 6.0KN is 0.043mm.load at yield point is 9.7KN at failure is 14.2KN ,reduction of the area is 45 percent. Calculate Young's modulus of elasticity, the yield stress and the ultimate stress
A tensile test is performed on a brass specimen 10mm in diameter using a gage lenght of 50mm. When the tensile load P reachers a value of 20kN, the distance between the gage marks has increased by 0.122 mm. What is the modulus of elasticity of the brass.
1. Titanium alloy with an elastic modulus of 107 GPa (15.5 x 106 psi) and an initial diameter of 3.8 mm (0.15 in. ), only elastic deformation occurs. If the maximum permissible elongation is 0.42 mm, find the specimen's maximum length before deformation (0.0165 in.) 2.) With a load of 89,000 N (20,000 lbf), a steel bar 100 mm (4.0 in.) long with a square cross section 20 mm (0.8 in.) on one edge is pulled in tension and undergoes an elongation of 0.10 mm (4.0 103 in.). Calculate the steel's elastic modulus, assuming the deformation is fully elastic. Please indicate the given sir. Thanks alot…
The stress-strain diagram of reinforcement steel having a cross-sectional diameter of 12 mm diameter and 100 mm gage length is determined after its tensile strength test as follows. Based on the stress-strain diagram determine the followings properties of the material (Poisson’s ratio of the material is 0.32) a) Resilienceb) Shear modulusc) Bulk modulusd) Ductility as described by the percent change in length
160 Upper scale A tensile test specimen of stainless steel alloy having a diameter of 0.550 in. and a gage length of 2.5 in. was tested to fracture. Stress and strain data obtained during 120 80 Lower scale the test are shown in the Figure Determine: (a) the modulus of elasticity. (b) the proportional limit. (c) the ultimate strength. (d) the yield strength (0.20% offset). (e) the fracture stress. 40 0.020 0.002 0.100 0.120 0.010 0.012 0.0 0.040 0.004 0.060 0.006 0.080 0.008 0.0 Strain (in./in.) Stress (ksi)
A ceramic matrix composite contains internal flaws as largeas0.001 cm in length. The plane strain fracture toughness of the composite is 45 MPaVm and the tensile strength is 550 MPa. Will the stress cause the composite to fail before the tensile strength is reached? Assume that f- 1.
A square specimen of Magnesium Oxide is loaded in a 3-point bending test. If w = h = 6.2 mm is the dimension necessary for it not to fracture when a load of 494.0 N is applied and the flexural strength is 117.1 MPa, determine the separation between the load points.
Please present FBD/s A tensile test is performed on a brass specimen 10mm in diameter using a gage lenght of 50mm. When the tensile load P reaches a valule of 20kN, the distance between the gage marks has increased by 0.122mm. What is the modulus of elasticitiy of the brass?