A blanking operation is to be performed to create the part shown below out of 2-mm thick half- hard 405 stainless steel. Provide (a) a drawing showing the punch dimensions; (b) a drawing showing the die dimensions; (c) the blanking force necessary. Note: you will need to translate tensile strength to shear based on the conversion from the text and use material properties from the text as well, tensile strength of 405 can be found in Ch. 6 (Metals). All dimensions noted below are in mm.

A blanking operation is to be performed to create the part shown below out of 2-mm thick half- hard 405 stainless steel. Provide (a) a drawing showing the punch dimensions; (b) a drawing showing the die dimensions; (c) the blanking force necessary. Note: you will need to translate tensile strength to shear based on the conversion from the text and use material properties from the text as well, tensile strength of 405 can be found in Ch. 6 (Metals). All dimensions noted below are in mm.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Manufacturer process A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength = 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking. Take: Ac=0.06
The casting shown is to be made in cast iron using a wood pattem. Perform the calculations required to determine the dimensions of the patten. Machining allowance, 3 mm / side, Shrinkage allowance for length/external 1 mm / 100 mm Shrinkage allowance for cored-hole 0.8 mm / 100 mm, Draft allowance external Imm / 100mm Draft allowance internal 2 mm / 100mm • 80 6 80 80 80 500 300 300 Final shape after all allowances are applied. 300 x 500 side at the top is on the parting plane. (All dimensions are in mm). You have to show calculations and dimensions at each stage.
A circular shape blank will be cut of mm diameter from a strip of mm with a clearance value of 0.25 mm. Take the shear strength as 400 MPa. Determine The appropriate punch diameter.Blanking force.Blanking force when the blade angle A circular shape blank will be cut of mm diameter from a strip of mm with a clearance value of 0.25 mm. Take the shear strength as 400 MPa. Determine The appropriate punch diameter.Blanking force.Blanking force when the blade angle is o.
Q1) Choose the correct answer in the following questions (some questions have multiple answers that are correct). 1. The appropriate punch size for a blanking operation using to perform a cold-rolled steel (half hard) circular part with diameter = 75.0 mm and 2.0 mm thick is: (a) Punch diameter = 77.72 mm and Die diameter = 74.50 mm. (b) Punch diameter = 73.50 mm and Die diameter = 75.50 mm. (c) Punch diameter = 74.70 mm and Die diameter = 75.0 mm. (d) Punch diameter = 75.62 mm and Die diameter = 76.0 mm. 2. In sheet metal processes, the typical of starting work geometry is: (a) high volume-to-area ratio. (b) low volume-to-area ratio. (c) equal volume-to-area ratio. 3. The characteristics of hot working relative to cold working are: (a) fracture of workpart is less likely, (b) friction is reduced, (c) increased strength properties, (d) isotropic mechanical properties, (e) less overall energy is required, (f) lower deformation forces are required, (g) more significant shape changes are…
A compound die will be used to blank and punch a large washer out of 6061ST aluminum alloy sheet stock 3.50 mm thick. The outside diameter of the washer is 50.0 mm and the inside diameter is 15.0 mm. Determine the punch and die sizes for the punching operation. TABLE 20.1 Clearance allowance value for three sheet-metal groups. Metal Group A. 1100S and 5052S aluminum alloys, all tempers 2024ST and 6061ST aluminum alloys; brass, all tempers; soft cold- 0.045 0.060 rolled steel, soft stainless steel Cold-rolled steel, half hard; stainless steel, half-hard and full-hard 0.075 Select one: a. 18.42 mm b. 20.42 mm c. 19.42 mm d. 15.42 mm
A compound die will be used to blank and punch a large washer out of 6061ST aluminum alloy sheet stock 3.50 mm thick. The outside diameter of the washer is 50.0 mm and the inside diameter is 15.0 mm. Determine (a) the punch and die sizes for the blanking operation, and (b) the punch and die sizes for the punching operation Vallue for allowance = 0.060
A mechanical press is powered by a 23-kW motor and operates at 40 strokes per minute. It uses a flywheel, so that the crankshaft speed does not vary appreciably during the stroke. If the stroke is 150 mm, what is the maxumum const.ant force rhat can be exerted over the entire stroke length?
16 30. Forging process is suitable for mass production. Select one: True False
0.075L T 0.8 4.0 -7.0 + All dimensions in inches -2.0- 0.1 T 0.205 0.25 T 0.25 5) Rolling: A rolling operation is performed on a 5 mm thick sheet of low carbon steel (K=530, n=0.26 from Table 8.1). The sheet is reduced by 0.2 mm each pass. The friction at the dies is 0.3. The roller diameters are 50 mm. The sheet width is 125 mm. a) Find the roll force for the 3rd pass. For the 3rd pass the initial thickness is 4.6 mm and the final thickness is 4.4 mm. a) Estimate the power to perform the 3rd pass if the roll rotates at 100 rpm.
Manufacturing Processes Q1. Chose the correct answer: 1. Which of the following are variations of sheet-metal-bending operations: (a) coining, (b) flanging, (c) hemming, (d) ironing, (e) notching, (f) shear spinning, (g) trimming, and (h) tube bending? 2. Springback in a sheet-metal-bending operation is the result of which one of the following: (a) elastic modulus of the metal, (b) elastic recovery of the metal, (c) overbending, (d) overstraining, or (e) yield strength of the metal? 3. The cutting force in a sheet-metal blanking operation depends on which mechanical property of the metal (one correct answer): (a) compressive strength, (b) modulus of elasticity, (c) shear strength, (d) strain rate, (e) tensile strength, or (f) yield strength? 4. A circular sheet-metal slug produced in a hole punching operation will have the same diameter as (a) the die opening or (b) the punch? 5. As sheet-metal stock hardness increases in a blanking operation, the clearance between punch and die should…
20. A forging process is shown at the figure below. Calculate the final diameter, if the initial diameter, initial height and final height are 20mm, 60mm and 40mm, respectively. FORCE ho h
2) A 2 mm thick metal sheet is to be bent at an angle of one radian with a bend radius of 100 mm. If the stretch factor is 0.5, the bend allowance is 99 mm 100 mm 101 mm 102 mm