A cylindrical specimen of some metal alloy having an elastic modulus of 101 GPa and an original cross-sectional diameter of 3.6 mm will experience only elastic deformation when a tensile load of 2430 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.41 mm. i mm

A cylindrical specimen of some metal alloy having an elastic modulus of 101 GPa and an original cross-sectional diameter of 3.6 mm will experience only elastic deformation when a tensile load of 2430 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.41 mm. i mm

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
Testing a round steel alloy bar with a diameter of 15 mm and a gauge length of 250 mm produced the stress–strain relationship shown in Figure Determinea. the elastic modulusb. the proportional limitc. the yield strength at a strain offset of 0.002d. the tensile strengthe. the magnitude of the load required to produce an increase in length of 0.38 mmf. the final deformation, if the specimen is unloaded after being strained by the amount specified in (e)g. In designing a typical structure made of this material, would you expect the stress applied in (e) reasonable? Why?
(b) (i) A tensile test specimen made from 0.4% C steel has a circular cross section of diameter d mm and a gauge length of 25 mm. When a load of 4500 N is applied during the test, the gauge length of the specimen extends to 25.02 mm. If the Young's Modulus of the steel is 199 GPa, calculate the diameter of the tensile test specimen used. 4
A tensile stress is applied along the long axis of a cylindrical aluminum rodwith a diameter of 10 mm. If the deformation is entirely elastic, determine themagnitude of the load required to produce a 2.5 X 10-3 mm change in diameter. Assume a modulus of elasticity of 70 GPa and a Poisson’s ratio of 0.33.
During a tensile test on a specimen of steel the following data was recorded, diameter of specimen 6.6mm gauge length of 50mm ,elongation of a load of 6.0 KN of 0.043mm. Reduction of area at failure of 45percent. Calculate the youngs modulus of elasticity ,the yield stress and the ultimate stress
3. The distribution of stress in an aluminum machine component is given (in megapascals) by Ox = y + z? Oy = x + z Oz = 3x + y Txy = 3z2 Tyz = x Txz = %3D Calculate the state of strain at a point positioned at (1,2,4). Use E=70 GPa and v = 0.3
This figure shows typical stress-strain behaviour for a brass. The inset figure shows the behaviour at low strains. 500 70 Tosle strength 450 MPa 166,000 ps 60 400 300 MP 40 30 200 Yeld steg 250 MPa (,0a 200 20아 100- 20 100 10 0.20 030 040 If the cylindrical test sample is initially 14cm long with an initial radius of 2mm, estimate the true stress in MPa at the ultimate tensile stress. (Enter your answer to the nearest whole number) an es