A flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.

A flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

(9,00 Puanlar) 36 - A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 25 cm, width = 15 cm, and thickness = 2,5 cm. If the total solidification time of the casting itself is known to be 4,5 min, determine the diameter of the riser so that it will take 2596 longer for the riser to solidify. Riser volume: V-(nD³/6 (D=diameter) Riser area: A-TD2 Casting volume: V-L-W-t (L-Length, W=width, t=thickness)
(9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with 8- length 50 cm, width = 35 cm, and thickness = 4 cm. If the total solidification time of the casting itself is known to be 7,5 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify. %3D Riser volume: V3(TD3)/6(D%3Ddiameter) Riser area: A=TD2 Casting volume: V-L-Wt (L-Length, W=width, t-thickness) a) 8,41 cm b) O 7,34 cm c) 6.62 cm 11,46 cm Boş bırak KÖnceki 8/43 Sonraki> Каpat
a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
A flat plate is to be cast in an open mold whose bottom has a square shape that is 200 mm by 200 mm. The mold is 40 mm deep. A total of 106 mm3 of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.0%. The linear shrinkage due to thermal contraction after solidification is 1.3%. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its 200 mm by 200 mm dimensions until solidification is completed, determine the final dimensions of the plate.
EX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.
4- A spherical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 20 cm  10 cm  2.0 cm. Previous observation have indicated that the total solidification time (TTS) for this casting = 3.5 min. determine the diameter of the riser so that it will take 25% longer for the riser to solidify
flו. 3D) امتحان شهري.pdf 1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 2. A mold sprue is 180 mm long, the cross-sectional area at its base is 2.4 cm?. The sprue feeds a horizontal runner leading into a mold cavity whose volume is 1600 cm?. Determine, volume rate of flow and time to fill the mold.
When casting a 4x10x20 in. Part, which has a top overflow with a H / D = 1.5 ratio, you want to determine the height and diameter of the overflow to prevent shrinkage in the part to be cast. Note: Remember that to achieve this, the overflow has to solidify some time after the piece has solidified, since in this case the overflow acts as a riser.
State the steps that must be taken to correct the following casting defects: 1. Formation of discontinuity in the casting.- 2. Cast surface consisting of a mixture of sand and metal. 3. Casting with balloon-shaped gas cavity near the surface. 4. Formation of hot tearing in expandable and permanent mold casungs. 5. Metal splatters during pouring and solid globules form and become entrapped in casting.
Problem 1 Suppose we want to cast a magnesium bar 20x20x45 mm³. We are to use a mid gating (exactly at the parting line) system with two runners and multiple ingates (no bends in runner), a top riser of 1:1.2 (D:H) ratio, and the bar lying down. The pouring cup to be used has a height of 10 mm. What would be the riser dimensions for this casting? Use the JB Caine Method (a, b, c = 0.10, 0.06, 1.08). If the choke area is 20 mm?, how long would the pouring time be?
A cast iron part with a square cross section is sand casted. Its length 14 in and the sides of the square cross section-2.5 in. If the mold constant in Chvorinov's rule - 3.6 min/in², how long, in minutes, will it take the casting to solidify?
(c) A square casting has a volume and surface area equal to 1000 mm³ and 600 mm² respectively, and a cylindrical riser through which the molten metal is poured has a volume and surface area equal to 282 mm³ and 244 mm² respectively. Using Chvorinov's rule, determine whether such a design would avoid shrinkage cavities.