Q1 : A rod made of carbon reinforced epoxy has a diameter 2.5 cm, length 1.25 m, and mass 0.95 kg. The carbon fibers have a modulus of elasticity 340 GPa and a density 1.91 g/cm'. The epoxy matrix has modulus of elasticity 4 GPa and a density 1.16 g/cm'. Assume there are no voids in the rod. What is the volume fraction of (a) the carbon fibers and (b) the epoxy matrix in the rod? Also, what is the predicted value for the modulus of elasticity in the (c) longitudinal direction and (d) direction perpendicular to the carbon fibers?

Q1 : A rod made of carbon reinforced epoxy has a diameter 2.5 cm, length 1.25 m, and mass 0.95 kg. The carbon fibers have a modulus of elasticity 340 GPa and a density 1.91 g/cm'. The epoxy matrix has modulus of elasticity 4 GPa and a density 1.16 g/cm'. Assume there are no voids in the rod. What is the volume fraction of (a) the carbon fibers and (b) the epoxy matrix in the rod? Also, what is the predicted value for the modulus of elasticity in the (c) longitudinal direction and (d) direction perpendicular to the carbon fibers?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

P2. Design a cylindrical thin-wall composite fuselage for storing compressed natural gas at a maximum operating pressure of 20 MPa. The pressure vessel is made by filament winding with fibres at ±45 degrees and is required to sustain three times the operating pressure without failure. The radius of the cylindrical pressure vessel must be 0.25 meters, and the length must be 2 meters. The maximum strengths of the composite ply are equal to 2000 MPa in the fibre direction and zero perpendicular to the fibre direction. Determine the minimum number of composite plies required to meet the design requirements. Hoop stress and longitudinal stress of cylinder are Answers: 38 plies (when tp=1 mm) t pr 21
Q2: A fiberglass composite consists of a matrix of vinyl ester and reinforcing fibers of E-glass. The volume fraction of E-glass is 30%. The density of the vinyl estiser 0.882 g/cm³, and its modulus of elasticity is 3.6 GPa. The density of E-glass is 2.6 g/cm³, and its modulus of elasticity is 76 GPa. A section of composite 1 cm by 25 cm by 2 m is fabricated with the E-glass fibers running longitudinally in the 2000 mm direction. Determine: (a) The masses of vinyl ester and E-glass fibers. (b) The density of the composite. (c) The composite modulus of elasticity in the longitudinal and the perpendicular directions of the glass fibers. (d) If the tensile strength of the glass fibers, is 1 GPA and the tensile strength of the epoxy matrix is 60 MPa, find the tensile strength of the composite in the longitudinal direction.
Q1: E-glass fibers reinforced epoxy matrix to fabricate a composite part. The volume fraction of fibers V, is equal the volume fraction of matrix V₁ and the modulus of elasticity of fibers E, is 55 times the modulus of elasticity of the matrix Em i. For the composite part how many times will be the longitudinal modulus of elasticity bigger than the transverse modulus of elasticity? ii. Find the ratio of the load carried by the fibers to the load carried by the matrix.
FIND: MODULUS OF RESILIENCE
The is a rope that just cannot stretch more than 0.6 cm from a tensile force of 500N without breaking. What is the minimum radius that the rope must have if it is .5kg and .6 meters long? The Young’s modulus for this material is 35*10^9 Pa.
5. A hollow cylinder has length 50.0 cm, internal diameter 5.0 cm and external diameter 6.0 cm. A force of magnitude 1.0 kN acts at each end of cylinder so that the cylinder is being compressed. Determine the compression of cylinder. (Ynollow cylinder = 7 x1010 Nm-2) [8.27 x10-6 m] 6. The water in a marine aquarium is 5 m deen.
A solid spherical material made of rubber with was exposed to a change in pressure of 85 Pa. Its volume reduced to 8.0 %. What is the Bulk modulus in Pa
5. A bone containing a solid polymer filler acting as an implant is tested by the application of a 2000N force to its midpoint. Assume the polymer is perfectly bonded to the bone. In the central region of the bone, the cross- section is approximately circular. For the cortical bone, E₂ = 20 GPa For the polymer, Ep = 1.8 GPa (a) Determine the location of the maximum bending moment in the system. .2m (b) Calculate the maximum bending stresses in the bone and in the polymer at the interface point H. 7.03 Mpa 78.13 Mpq along length For a circle, I = r²/4 from left relative to centroid end veslect small angle here P To = 12 mm 40 cm Bone, B |r₁ = 6 mm Solid Polymer fille Polymer, P
Find the breaking point along the fishing rod assuming that the base of the rod is in a fixed position and will not move. The rod is made out of Carbon fiber with diameters a=9.93 mm wide, b=7.13mm wide, and c=5.1mm wide. The total length of the rod is 2 meters. The modulus of elasticity of Carbon Fiber is 228 Gpa. Find what force "F" is needed to break the fishing rod assuming that the force is acting straight along the line. | 100 45 F
1.) A 200 kg load is hung on a wire of length 4 m, cross sectional area of 0.2 x 10 -4 m2 and Young’s modulus of 8 x 1010 Pa. What is its increase in length? 2.) When a beam 6 m long with a cross-sectional area of 19.4 cm2 is subjected to a compression force of 16 x 104 N, its length is shortened by 4.5 mm. What is the Young’s Modulus for the beam?
Q2: A composite component consists of a glass fiber and an epoxy matrix. The glass fiber weight fraction is triple of the epoxy weight fraction. Use the given properties of epoxy and glass to determine: 1. The composite axial modulus, transverse modulus, major Poisson's ratio, and in- plane shear modulus 2. If the total load is 24 kN and the applied stress is 60 MPa in this axial direction, compute the cross-sectional area of the composite and the magnitude of the load carried by each of the fiber and matrix phases. Given: Glass py-2.5 g/cm'. Ey-Ey-80 GPa, vy-0.2, G-38 GPa epoxy P 1.2 g/cm³, E-, E-3.5 GP, vy-0.3, G-1.35 GPa
Question 12 What is the resulting modulus of In (2 +3 j)?