a) The figure below shows three equilibrium structures that occur in an iron-carbon alloy, rank these from hardest to softest.b) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite. Relative mass to proeutectoid ferrite is 0.2 and pearlite is 0.80. How much carbon does this alloy contain? ProeutectoidFe3CPearliteEutectoid Fe3CFe3CFe3C-Eutectoid aa +Fe3C>PearliteProeutectoid a Temperature (°C)Temperature16001400120010001538°C600800 a84000(Fe)912°C1394°C1493°CY, Austenite0.022 Co0.76Ti U0.022a, Ferrite10.76V5C₁722.14Composition (at% C)15101147°Ca + FezCy+ Fe3C43Composition (wt% C)Xa + Fe3CLComposition (wt% C)4.30Y+Fe3C727°C20Cementite (Fe3C).56.7062525002000150010006.70Temperature (°F)

Answered: Image /qna-images/answer/fa83d281-cfff-48aa-b9b4-dbc10646ce42.jpg

a) The figure below shows three equilibrium structures that occur in an iron-carbon alloy, rank these from hardest to softest. b) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite. Relative mass to proeutectoid ferrite is 0.2 and pearlite is 0.80. How much carbon does this alloy contain?

a) The figure below shows three equilibrium structures that occur in an iron-carbon alloy, rank these from hardest to softest. b) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite. Relative mass to proeutectoid ferrite is 0.2 and pearlite is 0.80. How much carbon does this alloy contain?

Precision Machining Technology (MindTap Course List)

2nd Edition

ISBN:9781285444543

Author:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Publisher:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Chapter2: Measurement, Materials, And Safety

Section2.6: Metal Composition And Classification

Problem 14RQ: What is (are) the major alloying element(s) of 6061 aluminum?

See similar textbooks

Similar questions

An austenite containing 0.55% C was slowly cooled below 727°C, what would be its resulting microstructure? Composition (at% C) 10 15 20 25 1600 1538°C -1493 C L 1400 2500 1394°C 7+L 1200 1147°C 2.14 4.30 Y, Austenite 2000 1000 912°C y+ FezC 800 1500 727°C 0.76 0.022 600 `a, Ferrite a+ FegC Cementite (Fe;C). 1000 400 2 3 6.70 (Fe) Composition (wt% C) Temperature ("C) Temperature ("F)
If the Fe-C alloy consists of 62.29 % pearlite and 37.71 % proeutectoid cementite phase, what is the composition of the alloy in wt%
Indicate whether True/False. a) Interstitial solutes are effective in hardening FCC alloys but less effective than in BCC alloys.
An austenitic stainless steel contains - Ni. 12 - 15 % 8 - 12% O 15 - 18 % O 18 - 20 %
Match the steel microstructures to their names A B C
Of the following alloys, pick the one(s) thatmay be strengthened by heat treatment,cold work, or both: R50250 titanium, AZ31Bmagnesium, 6061 aluminum, C51000 phos-phor bronze, lead, 6150 steel, 304 stainlesssteel, and C17200 beryllium copper.
T or F -The α-phase is rich in iron. -The cementite phase is rich in iron -Pearlite steel has a lamellar microconstituent -AISI 1018 is a hypoeutecoid steel alloy -The Co of a hypoeutectic alloy is more than CE -Eutectoid means eutectic-like -Eutectic alloy means easy melting
E Questions? = = = 2. Where the carbon atoms sitting in BCT1 ma.rtensne a) Why does martensite has BCT structure?
According to Reference [1], alloys of nickel (Ni) and tungsten (W) are can form substitutional solid solutions up to approximately 11 at% W. Consider two different alloy compositions: Ni-5W (5 at% W) and Ni-10.5W (10.5 at% W). A. Which composition should be more ductile? B. Which composition should be stronger? C. Using the oy~ C¹/2 relationship from the lecture slides, how many times larger should the yield strength be for Ni-10.5W compared to Ni-5W? D. Where should the tungsten atoms sit relative to the dislocation on or opposite the side with the extra half-plane? You will need information from Appendixes of the textbook.
phase TÇF Iron -carbon phase diagram 2802°F (1539°C 1600 2912 L+ö 2719°F (1493°C) 1400 2552°F (1400°C) 0.16% Y+L, L+Fe3C 2192 4.3% 2097°F (1147°C) 2.06% 1200 Асм 1832 Аз. 1000 1670°F (910°C) Austețite + cementite+ledeburite Cementite + ledeburite 1472 800 1333°F(723°C) 0.025% 1112 p.83% A2= 1418"F(770°C) 600 752 A1, A2 400 Cementite + pearlite + transformed ledeburite 392 200 FezC 32 3 5 6 6.67% Carbon,% Figure Fe - C phase diagram Perlite+ferite Perlite+cementite
A 200g hypoeutectoid plain carbon steel contains 5.1wt% eutectoid ferrite. 1) What is its average carbon content in weight? 2) What is the weight of total ferrite? 1600 8+7 Liquid 1400 L+ Fe;C L+y 1200 1148°C y austenite 1000 2.0 4.3 y + Fe,C 800 e 723°C 600 0.8 0.02 400 a + Fe,C Fe;C 200 0% C 100% Fe 6 6.67 Fe,C 3 4 Weight percent carbon Temperature ("C)
The carbon percentage of AlISI 4340 steel is O A. 0.40% O B. 0.43%. OC.0.0% O D.0.34%