ASteel bar of (25mm) diameter was tested in tension and results were recorded as Load at Yield 218.13KN,Ultimate load (278.2KN).The Elongation measured over gauge length of (100mm) was ( 12.62mm)at Fracture point and minimum diameter was (23.64mm) determine Yield stress,Ultimate stress,%Elongation, * %rudection in area ث إضافة ملف

ASteel bar of (25mm) diameter was tested in tension and results were recorded as Load at Yield 218.13KN,Ultimate load (278.2KN).The Elongation measured over gauge length of (100mm) was ( 12.62mm)at Fracture point and minimum diameter was (23.64mm) determine Yield stress,Ultimate stress,%Elongation, * %rudection in area ث إضافة ملف

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The table below shows the deformation data that resulted from applying a pure tensile load to a brass alloy rod with an initial length of 30 mm and a diameter of 10 mm. This rod was subjected to necking and beyond necking deformation. The data at fracture is shown in the last row. Applied Load (N) Length (mm) Diameter (mm) 75,100 33.8 68, 250 34.9 50,200 35.7 6.7 Solve for the TRUE STRESS/ES and TRUE STRAINS. 8.3 7.8
ASAP
Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. What tension force is required to cause yielding in a bar of the same material but with a diameter of 20 mm? P, kN AL mm 7.22 0.0839 14.34 0.1636 21.06 26.8 31.7 34.1 35.0 0.241 0.308 0.380 0.484 0.614 36.0 0.924 36.5 1.279 36.9 37.2 1.622 1.994
Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. Determine the yield strength with offset limit, and %total elongation. P, kN AL mm 7.22 14.34 0.0839 0.1636 21.06 0.241 26.8 0.308 31.7 0.380 34.1 0.484 35.0 0.614 36.0 0.924 36.5 1.279 36.9 1.622 37.2 1.994
yields under a load of 8KN; it attains a max load of 15KN and breaks finally A tensile test is carried out on a bar of mild steel of diameter 20mm. The bar Еxample at a load of 7KN. Estimate yP (i) The tensile stress at the yield point (ii) The ultimate tensile test ii. Max loa (iii) The average stress at the breaking point if the diameter of neck is Omm.
A sample test rod made of a ferrous material of 0.5 in. diameter was tested for tensile strength with the gauge length of 2.5 in. The following observations were recorded: Final length = 3.15 in; Final diameter = 0.275 in; Yield load = 7650 lb. and Ultimate load = 10375 lb. (a) Calculate: 1. yield stress, 2. ultimate tensile stress, 3. percentage reduction in area, and 4. percentage elongation. (b) What specific material, if any, is similar to this tested rod? Refer to AT7 and AT8. (c) This same material is then used as a tension member 55 inches long and is subjected to a maximum load of 6000 lb, repeated but not reversed. (d) Solve part (c) if the total elongation is not to exceed 0.025 in.? 1. %3D
The results of a tensile test are: Diameter of the specimen Gauge length Load at limit of Proportionality Extension at the limit of Proportionality Maximum Load : 10mm :40 mm : 70kN :0.08mm. :100 kN Calculate stress at limit of proportionality and young's modulus.
Given: Metal Specimen diameter x-sectiion (circular)= 0.55 in Gage Length= 2.030 in Fracture bccurved at 28,500 pounds final length= 2.30 in Final diameter= 0.43 in Determine: a) Ultimate tensile stress in ksi
C1. A mild steel tensile specimen of initial length 41 mm and initial diameter 6.2 mm is subjected to a tensile test and the following data are obtained. Yield Strength as 115 MPa Maximum Strength as 210 MPa Fracture Strength as 168 MPa Percentage of Elongation as 50 % Percentage of Reduction in area as 32% Determine the Final length, Final area, Yield load, Ultimate load & Fracture load. The yield load in N is The Ultimate load in N is The Fracture load in N is
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm The % reduction in area is * O 15.819% 18.819 O 17.819 O 20.819
The results of a tensile test are: Diameter of the specimen Gauge length Load at limit of Proportionality Extension at the limit of Proportionality Maximum Load : 10mm :40 mm :80kN : 0.06mm. :100 kN Calculate ultimate tensile stress and young's modulus.