Plz do it correct I will give you update. Using the above theory estimate the factor of safety for a certain type of steel whose Proportional limits 280 MPa. The principal stresses were found to be 100 MPa (tensile), 60 MPa (tensile) and 30 MPacompressive).

Answered: Image /qna-images/answer/0ba6aaac-a23f-403b-b67c-b71b1155d258.jpg

Answered: Certain type of steel whose…

Certain type of steel whose Proportional limit the above theðry sing n The principal stresses were found to be 100 MPa (tensile), 60 MPa (tensile) and 30 MPa ompressive).

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Tensile and fully reversed loading fatigue tests were conducted for a certain steelalloy and revealed the tensile strength and endurance limit to be 1200 and 550 MPa,respectively. If a rod of this material supply were subjected to a static stress of 600MPa and fully-reversed oscillating stresses whose total range was 700 MPa. Assuming garber relationship will this rod fail by fatigue failure
1. A steel of rotating-beam test specimen has an ultimate strength of 1600Mpa. Estimate the life of the specimen if it is tested at a completely reversed stress amplitude of 900MPA. Hint: You can either extrapolate the curve of f vs. Sut, or use the equation derived on P10 to estimate the value of f.
2. A steel of rotating-beam test specimen has an ultimate strength of 1100Mpa. Estimate the fatigue strength of the specimen corresponding to a life of 150k cycles of stress reversal.
A high-strength steel has a yield strength of 1,460 MPa and a KIC of 98 MPa √m. Calculate the size of a surface crack that will lead to catastrophic failure at an applied stress of 3/4Y.S.
1. A ductile hot-rolled steel bar has a yield strength in tension and compression of 350 MPa. Using the distortion-energy and maximum-shear-stress theories, determine the factors of safety for the following plane stress state: 75 MPa 50 MPa 50 MPa 2. Consider a bar of AISI 1015 cold-drawn steel. Using the distortion-energy and maximum-shear-stress theories to determine the factors of safety for a stress state with the following plane principal stresses: 0A = 30 kpsi, OB = 15 kpsi.
Case Study Calculate the Tensile Toughness Tensile toughness measures the total energy absorbed prior to fracture and is different from fracture toughness and impact toughness. Fracture toughness measures the resistance to fracture when a flaw (i.e. crack) is present in the material. Since it is nearly impossible and costly to manufacture materials with zero or near zero defects, fracture toughness is a major consideration for all structural materials. Impact toughness measures a materials ability to withstand an impact blow (i.e. high strain rates) and is particularly important in assessing the ductile-to-brittle transition behavior (more details later). Impact toughness is also commonly referred to as notch toughness. The tensile toughness can be estimated using the stress-strain curve by measuring the area under the curve (both the elastic and plastic regions). Tensile Toughness = f Stress, σ Ty- Ey Efracture ETS Ur Ey Efracture o de = U₁ + SETS o de + Sefracture o de Ey Ey o de =…
Given: Stress strain curve of 10 mm diameter and 1 m long ductile stainless-steel rod. 900 800 700 600 500 Mild 400 Stainless 300 200 - 100 0.1 0.2 0.3 0.4 Strain 0.5 0.6 0.7 Draw stress-strain curve for compression here 1. Label all points of significance on the stress strain curve 2. Draw the stress-strain curve for the rod in compression and label all points of significance. 3. What is the Young's modulus in tension? Assume .001 strain at 500 MPa 4. What is its Youngʻs modulus in compression? 5. What is the tensile yield strength of this rod using the 0.2% offset criteria? 6. What is the compressive yield strength of the rod? 7. What is force required to yield the rod?. Show calculation: 8. What is the UTS of this rod?. 9. What is the force required to break the rod? Show calculation: 10. What will be UCS of the rod? Stress (MPa)
a)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?
Let's assume that the stress-strain elongation curve of a high-strength steel is given by this equation. o = 1.4*10º"ɛ 3 2.9*10*ɛ ² + 2.1*10°z Calculate the yield limit value of this steel. Oa (kgf/cm³) (For Yield Strength, use a straight line from the starting point and Calculate wwwwwww ww w m by moving the line parallel to the given curve)
Q3b. The stress-strain characteristic curves for materials A, B and C are shown below. Which one statement most accurately describes the relative toughness and ductility for materials A, B & C? Material A Material B Material C Strain Select one: a. Material A has low toughness, Material B has high ductility and Material C has low toughness. b. Material A has high toughness, Material B has low ductility and Material C has low toughness. c. Material A has low ductility, Material B has low toughness and Material C has low toughness. d. Material A has high ductility, Material B has low toughness and Material C has high toughness. Stress
140 900 1040 Steel Percent cold work = 0 %3D 120 Yield strength = 200 MPa 800 Yield strength = 29 ksi 700 100 600 Brass -80 500 400 60 Copper 300 40 200 10 20 40 30 50 60 70 Percent cold work Tensile strength (MPa) Tensile strength (ksi)
Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?