A composite with a vinyl ester (VE) matrix contains 2 vol% CNTS with the followingcharacteristics: 1= 7 um, d= 50 nm, di = 4 nm, and EcCNT = 900 GPa. The modulus of the VEmatrix is 1.9 GPa.%3Dc. Find the Major Poisson's ratio for this composite using strength of materials approach.d. Find the in-plane shear modulus for this composite using strength of materials approach.

data providded Em=1.9 GPaEf = 900 GPa Vm =matrix volume fraction =0.98Vf =fiber volume fraction…

Answered: d%3D50 nm, di = 4 nm, and ECNT oisson's…

Engineering

Mechanical Engineering

d%3D50 nm, di = 4 nm, and ECNT oisson's ratio for this composite using strength of material

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Glass fibres provide longitudinal reinforcement for a nylon material subject to tensile load. The fibre diameter is 20 μm and the volume fraction is 0.45. (Take Young’s modulus of glass fibres as 70 000 MPa and nylon as 2800 MPa)(i)Calculate the Young’s modulus of composite(ii)Determine the tensile strength in the glass fibre if the tensile strength of the composites and matrix is 14 MPa and 11.8 MPa, respectively
(B) Composite consists of polyester as a matrix reinforced by glass fiber. If the composite have cross- sectional area is (250 mm') and stress of (50 MPa) is applied in this longitudinal direction. 1-Compute the weight fraction of fibers and matrix. 2-Compute the magnitude of the load carried by each of fiber and matrix phase. Note:- Modulus of Elasticity (GPa) Material Density (g/cm³) Polyester 1.38 3.4 Glass Fiber 2.58 69 Composite 2.1
A discontinuous fibre reinforced composite consists of 20mm long carbon fibres in a polymer matrix. The volume fraction of the composite is 0.5, interfacial shear strength 5MPa and the critical fibre length 2.5mm. The fibre modulus is 250GPa and strain to failure 1.5%. The matrix modulus is 3.5GPa and failure strain 10%. Calculate the tensile strength of the composite in the fibre direction. Answer: 3564
1. An element of graphite-reinforced composite is completely dry and is constrained against any dimensional changes in the 1 and 2 directions, but it is free to expand in the 3 direction. The element absorbs 1.5% of its dry weight in the form of moisture. (a) What is the strain in the 3 direction as a result of the moisture absorption? Why is this strain different from the value given by B3AM? (b) What stresses develop in the element? Assume that moisture absorption does not influence the material properties.
3- Derive the rule-of-mixtures equation (α₂ = α{V¹ + a²Vm) for the coefficient of thermal expansion α₂. Compare the variation of a₂ based on rule-of-mixtures & alternative rule with fiber volume fraction for graphite-reinforced material (use numerical values of question 1 for fiber and matrix properties).
Question 2 = 219,48 M//a = 247,3785 Pa 2.1 Consider a polymer reinforced with Spectra 1000 fibers, with a fiber volume ratio of x = 15 %. For a cross sectional area of 130 mm² and a load of 250 kg, calculate the stress in the fibers and in the matrix if the matrix material is polycarbonate. 2.2 Why are fibres capable of supporting a large portion of the tensile load in composite materials?
Question Seven (Plastics) The data below is from a fibre reinforced plastic. Would this composite be suitable for use at 400°C? Explain your answer. Temperature (°C) 20 100 200 300 400 500 600 Plastic A Plastic B Plastic C Yield Strength (MPa) 270 350 47 Tensile Strength (MPa) 300 500 52 E (GPa) 130 3 14 115 100 95 Question Eight (Plastics) Identify the thermoplastic, the elastomer and the thermoset. 70 58 0 Young's Modulus (GPa) Elongation (%) 12 3 600
For a glass/epoxy lamina with a 70% fiber volume fraction using the properties in the tables provided below (a) Find the ultimate tensile strength. (b) Find the minimum and critical fiber volume fractions related to (a). (c) Find the compressive strength when the matrix undergoes extension mode and when the matrix undergoes shear mode, which one controls the compressive failure? Property Axial modulus Transverse modulus Axial Poisson's ratio Transverse Poisson's ratio Shear modulus Axial tensile strength Axial compressive strength Transverse tensile strength Transverse compressive strength Shear strength Epoxy Glass Units 3.4 85 GPa 3.4 85 GPa 0.3 0.20 0.3 0.20 1.308 35.42 GPa 72 1550 MPa 102 1550 MPa 72 1550 MPa 102 1550 MPa 34 35 MPa
A continuous and aligned glass fiber-reinforced composite with modulus of elasticity of 55 GPa. The volume fiber fraction is 40 and the modulus of elasticity of the fiber is 75 GPa. Calculate the volume fraction of epoxy matrix if you know the modulus of elasticity of the modulus of elasticity of the matrix is 2.5 GPa and then determine the strain that is sustained by each phase under applied stress of 27 Mpa. (assume that the cross-section area is 150 mm2)
V. Using the figure/data below, answer the following questions for polystyrene: (a) What is the specific free volume at 120°C? (b) What is the specific free volume at 80°C? ag "24 x 104 1ºc OR "55x 104 10C Spacific Volume 100°C Temperature, OC
An aligned and continuous glass fiber-reinforced epoxy composite consisting of 55 vol% glass fibers has a cross-sectional area of 420 mm2. The composite is subjected to a longitudinal load of 61,300 N. Calculate the magnitude of the stress on matrix phase if the elastic moduli of the glass fiber and the epoxy are 165 GPa and 5.7 GPa, respectively.
For a given polymer, the activation energy for the stress relaxation was measured to be 59kj/mol. If the stress relaxation time for this polymer at 7 degree Celsius is 3150 seconds. What is the relaxation time at 110 degree Celsius