i) Explain the Tresca and Von Mises criteria in crystal plasticity and their role in the design of engineering structures. What is the equivalent stress org in the von Mises criterion? ii) Explain in detail the topological aspects (Elastic vs Plastic regions) of graphs (a) and (b) in the figure below in terms of yielding conditions in a multi-axial state of stress. Fig.3 do (b)

i) Explain the Tresca and Von Mises criteria in crystal plasticity and their role in the design of engineering structures. What is the equivalent stress org in the von Mises criterion? ii) Explain in detail the topological aspects (Elastic vs Plastic regions) of graphs (a) and (b) in the figure below in terms of yielding conditions in a multi-axial state of stress. Fig.3 do (b)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

For the images shown below, which Miller indices for crystallographic planes are included? lu C. Z Select one or more: a. (111) b. (230) (211) d. (110) e. (100) b y X a/2 Z b Z 2b/3
A crime scene analyst found out a 10 mm thick metal plate was penetrated by 10 bullets that caused (c) a severe but clean volumetric defect in the form of 10 holes with a diameter of 10 mm each. If the theoretical density of the metal plate is 10 g/cm³, how many metal atoms have been removed from the plate due to the impact? Assume a solid structured metal, with an atomic weight of 100 g/mol, Given the Avogadro constant as 6 x 1023 atom/mol and a = 3.14.
4) Express very briefly why the first region (Primary Creep) in Strain-Time creep diagram can be a design limitation (for what type of applications in general? Please DO NOT write aircraft parts!).: 5) For what type pf applications secondary creep range in Strain-Time creep diagram can be considered as design range?: 6) Would ceramic materials or metallic materials would have better creep resistance? Briefly explain why?: 7) Explain why the crystal structure (lattice type) is related to creep resistance?
Q(4): Fill in the blanks of the following (Only Ten) 1. The stress and strain of a sample under mechanical testing can be classified into two types ------ and ------. 2. Dislocations in the real crystal can be classified into two groups based on their geometry it is ------ and ----- 3. Interstitial imperfection will act as a face resistance for moving of - ----- making it difficult to create permanent deformation in metals and alloys. 4. The error function of Erf (-x), is equal to 5. At the yield point or the proportional limit point, the deformation in this region is of the type ----- 6. There are two type of vacancy mechanism for atomic diffusion ---- -- and ------. 7. In no steady-state diffusion, the and the ----- at some particular point in a solid vary with time. 8. If exciton is localized, it is known as ------, and if it extends along a large number of repeating molecule units, then it is known as the -- 9. Elastic limit can be defined as ---- 10. The diffusion coefficient for…
derive the generalized hook's law for an isotropic homogeneous elastic solid in terms of lame's constats
Televio olpn Example moleda Sblaiy Ieteyo elpnie erli lliW (B Q.: A stress of 75 MPa is applied in the [001] direction on an fcc single crvstel Calculate: T. (a) the resolved shear stress acting on the (111) [-101] slip system and, (b) the resolved shear stress acting on the (111) [-110] slip system.
Help me please
Consider an iron single crystal with CCC crystal structure oriented in such a way that a tensile stress is applied to the along one direction [010]. a) Calculate the shear stress resolved along a plane (110) and a direction when a tensile stress of 52 MPa is applied. The normal to the slip plane forms 45° with traction direction. the direction of slip forms 55º with the traction direction. b) If the slip occurs in one plane (110) and in one direction and the critical resolved shear stress is 30 MPa, calculate the magnitude of tensile stress that must be applied to initiate the flow.
Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [11 2] direction. If slip occurs on a ( 111) plane and in a [0 11] direction, and the crystal yields at a stress of 5.12 MPa, compute the critical resolved shear stress. CRITICAL RESOLVED SHEAR STRESS • CRITICAL RESOLVED SHEAR STRESS (T, THE MOST FAVORABLY ORIENTED SLIP SYSTEM WHEN SHEAR STRESS IS AT J: SLIP IN A SYSTEM STARTS ON CRSS THIS CRITICAL VALUE • MINIMUM SHEAR STRESS REQUIRED TO INITIATE SLIP • SINGLE CRYSTAL PLASTICALLY DEFORMS WHEN: T, > T, CRSS OR TR(max) =T CRSS 'R Tcrss (cos o cos A)max
Consider an iron single crystal with CCC crystal structure oriented in such a way that a tensile stress is applied to the along one direction [010]. a) Calculate the shear stress resolved along a plane (110) and a direction [11] when a tensile stress of 52 MPa is applied. The normal to the slip plane foms 45° with traction direction. the direction of slip forms 55° with the traction direction. b) If the slip occurs in one plane (110) and in one direction [ī11] and the critical resolved shear stress is 30 MPa, calculate the magnitude of tensile stress that must be applied to initiate the flow.
Potassium (K) has the Body-Centered Cubic (BCC) crystal structure. The edge length is a = 0.533 nm. What is the linear density in atoms/nm along direction [011P Select one: a. 4.50 b. 6.37 O C. 3.18 d. 7.48 O e. 1.33 Europium has the Body-Centered Cubic (BCC) crystal structure shown in the figure below. The radius of the Europium atom is r= 0.204 nm. What is the planar density in atoms/nm in plane (20)? Plane (200)
Help me please