Questions 30 is based on the information below: An asphalt concrete mix design has the following properties. The densities of the binder and aggregate are 1.090 g/cm³ and 2.760 g/cm³, respectively. The bulk density of the entire mix is 2.220 g/cm³. The percent binder content is 6.2% (by weight). Assume no absorption. V₁= 1.0 cm³ Volume Vv Vb Vs AIR Binder Aggregate Mass Mb Ms Mt 30. As an engineer, you are asked to use this mix design for a 25 kilometer-long section of roadway where the total pavement width is 8.0 meters and the thickness is 15 centimeters. What is the (a) total volume of binder and (b) the total volume of aggregate that you would need to purchase? Also, determine the (c) total %air voids in the mix.

Questions 30 is based on the information below: An asphalt concrete mix design has the following properties. The densities of the binder and aggregate are 1.090 g/cm³ and 2.760 g/cm³, respectively. The bulk density of the entire mix is 2.220 g/cm³. The percent binder content is 6.2% (by weight). Assume no absorption. V₁= 1.0 cm³ Volume Vv Vb Vs AIR Binder Aggregate Mass Mb Ms Mt 30. As an engineer, you are asked to use this mix design for a 25 kilometer-long section of roadway where the total pavement width is 8.0 meters and the thickness is 15 centimeters. What is the (a) total volume of binder and (b) the total volume of aggregate that you would need to purchase? Also, determine the (c) total %air voids in the mix.

Traffic and Highway Engineering

5th Edition

ISBN:9781305156241

Author:Garber, Nicholas J.

Publisher:Garber, Nicholas J.

Chapter18: Bituminous Materials

Section: Chapter Questions

Problem 12P

See similar textbooks

Similar questions

Given the following information from an asphalt mix: Gsb = 2.705 Gmm = 2.534 Gmb = 2.432 Gb = 1.014 Pb = 5.7% Unit weight of water = 62.4 Ib/ft3 Assume 1 ft for total volume. Draw mass/volume relationship and determine Mass of Mix (Mm) Ib., Mass of Binder (Mb) Ib., Volume of Binder (Vb) pcf, Volume of Void-less Mix (Vmm) Volume of Air (Va) pcf, Volume of Absorbed Asphalt (Vba) pcf, Volume of Effective Asphalt (Vbe) pcf. In addition, calculate Air Voids (VA) %, Voids in Mineral Aggregate (VMA) %, and Voids Filled with Asphalt (VFA)
An asphalt concrete specimen has the following properties: • Asphalt content = 5.5% by total %3D weight of mix • Bulk specific gravity of the mix = 2.475 • Theoretical maximum specific of gravity = 2.563 • Bulk specific gravity aggregate = %3D 2.689 Ignoring absorption, compute the percent VFA Select one: A. 67.2% B. 68.1% C. 76.3% D. 73.8%
For the given concrete mix design below, calculate the field weight of the ingredients in kg's if the absorption capacities of both aggregates are 2% and both aggregates became oven dry after a very sunny day? Weight in kg per m³ 300 Ingredient Cement Water SSD Coarse aggregate SSD Fine aggregate Water: Seç Coarse aggregate: Seç Fine aggregate: Seç... → + 150 1020 816
A mix design requires 1160 kg/m3 of coarse aggregate (in dry condition), 599 kg/m3of fine aggregate (in dry condition) and 148 kg/m3 of water. The absorption capacityof the coarse aggregate is 0.4 % while the moisture content is 1.5%. The absorptioncapacity of the fine aggregate is 0.4 % while the moisture content is 4%. Pleaseanswer the following questions based on information given. a. What is the amount of Moist Coarse Aggregate? b. What is the amount of SSD Fine Aggregate? c. What is the amount of Moist Fine Aggregate? d. What is the amount of water after adjusting for moisture?
The mix design for an asphalt concrete mixture requires 2 to 6% minus 0.075 mm. The three aggregates shown in Table P.5.34 are available. TABLE P5.34 Minus 0.075 mm Coarse 0.5% Intermediate 1.5% Fine Aggregate 11.5% Considering that approximately equal amounts of coarse and intermediate aggregate will be used in the mix, what is the percentage of fine aggregate that will give a resulting minus 0.075 mm in the mixture in the middle of the range, about 4%?
For the given concrete mix design below, calculate the field weight of the ingredients in kg's if the absorption capacities of both aggregates are 1%, total moisture content of coarse aggregate is 2% and the total moisture content of fine aggregate is 4%? Ingredient Weight in kg per m³ Cement 300 Water 150 1000 800 SSD Coarse aggregate SSD Fine aggregate Fine aggregate: Seç... ÷ Coarse aggregate: Seç... Seç Water: + ÷
In designing a concrete mix, if the amount of mixing water is estimated at W = 185 Kg/m, the SSD weight of the coarse aggregate is 1045 Kg/m, and the SSD weight of the fine aggregate is 617 Kg/m. The coarse aggregate has a moisture content of 1% and an absorption capacity of 2%. The fine aggregate has a moisture content of 2% and an absorption capacity of 5%. The adjusted weight of mixing water (in Kg/m³) is: O 177 O 214 156 193 O 172 O O O O O
An asphalt concrete specimen has the following properties:asphalt content = 5.9% by total weight of mix bulk specific gravity of the mix = 2.457 theoretical maximum specific gravity = 2.598 bulk specific gravity of aggregate = 2.692Calculate the percents VTM, VMA, and VFA.
A civil engineer wants to design a concrete mix design with the following criteria: Design a concrete strength: 25 MPa with a slump of 90 mm. Ignore the need for exposure Select a non-air entrained concrete Fine aggregates properties: Fineness modulus 2.67; Bulk specific gravity 2.66 Coarse aggregates properties: Maximum size aggregate of 25 mm with the bulk specific gravity 2.55 and dry-rodded mass 2000 kg/m3. Based on the criteria above 2.1. Calculate the required strength. 2.2. Calculate the water cement ratio. 2.3. Calculate the mix proportions of all materials including cement, water, fine aggregates, coarse aggregates, and air content for 1 m3.
Consider the mix proportions of the concrete given in the table below: Portland Component Aggregate (coarse Superplasticizer or & fine) Water cement cement substituents kg/m3 700 500 800 This concrete is to be used in a construction site where the designer and client have asked for a concrete mix with the following specifications: • The mix will have to be cost-effective • The environmental impact of concrete is of paramount importance to the client, and so the lower the carbon footprint of the concrete, the better. • Strength is also important, and so strategies for improving strength are welcomed. • The mix will be used to build steel reinforced structures for the ventilation shafts of a new sanitary sewer system in Sheffield, where the concrete will be exposed to acidic water. Therefore. special attention has to be paid to the durability of concrete. Explain two changes you would make to the mix proportions given in this photo to improve the strength and durability but be cost…
Use the following volumetric relationships for asphalt mix analysis: VTM = 100 (1 - Gmb) VFA = 100 3. An asphalt concrete specimen has the following properties: Asphalt content = 5.5 % by total weigh of mix Bulk specific gravity of the mix = 2.475 Theoretical maximum specific gravity = 2.563 Bulk specific gravity of aggregate = 2.689 Assuming there is no absorption of binder, calculate the following: (a) Percent Voids in Total Mix (b) Percent Voids in Mineral Aggregate: VMA – VTM VMA (c) Percent Voids filled with asphalt: VMA = = (100 - Gmb Ps Gsb
A compacted asphalt concrete specimen has the following properties:a. Asphalt content = 5% by total weight of the mixb. Bulk specific gravity of the mix = 2.500c. Theoretical maximum specific gravity = 2.610d. Bulk specific gravity of the aggregate = 2.725 Ignoring absorption, compute the percents VTM, VMA, and VFA.