400300200100AlR1017.12036.13059.866.7405060Weight percentage, magnesiumAl-Mg phase diagram704378087.490MgWhat is the maximum solubility, in wt% , for Mg in y? (Give your answer as a number only to 1 decimal place) Temperature (°C)200100(Pb)Add your answer18.320+L183°C40a + B61.960Composition (wt% Sn)BIL80232°C97.8500400300200100100(Sn)Temperature (F)A Pb-40 wt% Sn solder is slowly cooled from 300 °C. What will be the fraction of liquid present at 184 °C(i.e. just above the eutectic temperature)? Give your answer to 2 decimal places.I

For the solution refer below images.

Temperature (C 200 100 (Pb) Add your answer a+L 18.3 20 183°C 40 619 60 Composition (wt% Sn) P+L 80 232-C 97.8 500 400 300 200 100 100 (SA) Temperature (F) A Pb-40 wt% Sn solder is slowly cooled from 300 °C. What will be the fraction of liquid present at 184 °C (ie. just above the eutectic temperature)? Give your answer to 2 decimal places. I

Temperature (C 200 100 (Pb) Add your answer a+L 18.3 20 183°C 40 619 60 Composition (wt% Sn) P+L 80 232-C 97.8 500 400 300 200 100 100 (SA) Temperature (F) A Pb-40 wt% Sn solder is slowly cooled from 300 °C. What will be the fraction of liquid present at 184 °C (ie. just above the eutectic temperature)? Give your answer to 2 decimal places. I

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…
2. a) How many kilograms of nickel must be added to 1.75 kg of copper to yield a liquidus temperature of 1300 °C? b) How many kilograms of nickel must be added to 5.43 kg of copper to yield a solidus temperature of 1200 °C? c) The solidus and liquidus temperatures for the copper-gold system are given here. Construct the phase diagram for this system and label each region. Composition (wt.% Au) Solidus Temperature (C) Liquidus Temperature (C) 1085 1085 1019 972 20 1042 996 946 40 60 934 80 911 911 90 928 942 95 974 984 100 1064 1064
Q1 / Two metals Beryllium (Be) and Silicon (Si) have melting points 1282°C and 1414 °C respectively, are completely soluble as liquids but completely insoluble as solids . They form a eutectic at 1090°C containing 61 wt% Si -39wt% Be? Determine the following:- 1- Draw the thermal equilibrium phase diagram and identify all phases are present in diagram ,then sketches what happens in microstructure when the alloys containing , a- 10wt% Si, b-70wt%Si , solidify completely. 2- Determine the composition and the amount of each phase for the alloy which contain 15 wt% Si-85wt% Be at 1150°C If the alloy is hypoeutectic determine the amount of eutectic at 600 °C? or hypereutectic and
Consider Cu - Ag Phase diagram below: 1200 A -Liquidus 1000 Liquid -Solidus 779°C (TE) 800 Temperature (°C) 600 400 a C 200 0 B 8.0 (Cag) Solvus a +L a + ß E 71.9 (CE) B+L 91.2 (CBE) B H 1 1 1 1 1 { ( L 20 40 60 80 100 (Cu) Composition (wt% Ag) (Ag) Consider 71.9% Ag-28.1% Cu, which is cooled below 779°C. What is the composition of the phases present just below 779°C and give the amount of beta phase present
For alloy of two hypothetical metals A and B, there exist an a, A-rich phase and a B, B-rich phase. For alloys of two different overall compositions at 25°C, the weight fractions of Wa and WB are listed in the table. Determine the solubility limits for both a and B phases at 25°C. Alloy Composition Wa WB 70wt% A-30wt% B 0.78 0.22 35wt% A-65wt% B 0.36 0.64
Figure 1 shows the Mg/Pb phase diagram. 700 L L 600 + M a + L Mg, Pb 500 465 400 L. Mg Pb 300 200 a + Mg Pb B+ Mg Pb 100 20 40 60 80 100 Mg Composition (wt% Pb) Pb Mg Pb Figure 1 The Mg/Pb phase diagram QUESTION 1-A Show on the diagram the following: 1. The Pb% to gain alpha grain with Mg.Pb on the boundary of alpha at the room temperature 2. Is it possible to gain beta grain with Mg.Pb on the boundary at the room temperature of an alloy? Explain 3. What is the mount of alpha in an alloy (50%Mg +50%Pb) at temperature of 500°C? 4. What is the mount of alpha in the alloy (50%Mg +50%Pb) at the room temperature? 5. What is Mg2Pb? Explain 6. If the requirement for an alloy to have 100 pph eutectic at the room temperature, what is the metal Pb percent? 7. Is it possible to have an alloy containing beta and alpha at the room temperature? Explain Temperature (°C)
Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.
A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °℃
The figure below shows Pb-Sn phase diagram. What is the composition of Pb and Sn at point 1? 1200 1000 Liquid a +L 779 C (Tg) B+L 6 800 8.0 71.9 G 91.2 600 400 200 20 40 60 80 100 (Pb) Composition (wt% Sni (Sn) Callister Jr., W.D., 2007 O a. 80 wt % Sn and 20 wt % Pb O b. 10 wt % Sn and 90 wt % Pb O c. 90 wt % Sn and 10 wt % Pb O d. 20 wt % Sn and 80 wt % Pb Temperature ("C)