Q3: A tensile test on a cold worked brass gave the following results. The diameter of the test specimen d= 16 mm and the gauge lenth was 80 mm After fracture the gauge length was 85 mm and the fracture point was was 15 mm diameter. The maxiumu load was 150 KN. The load and extension at the elastic limit were 70 KN and 0.5 mm, respectively. Calculate the modulus o elasticity. Calculate the % of elongation and % of reduced cross sectiona area

Q3: A tensile test on a cold worked brass gave the following results. The diameter of the test specimen d= 16 mm and the gauge lenth was 80 mm After fracture the gauge length was 85 mm and the fracture point was was 15 mm diameter. The maxiumu load was 150 KN. The load and extension at the elastic limit were 70 KN and 0.5 mm, respectively. Calculate the modulus o elasticity. Calculate the % of elongation and % of reduced cross sectiona area

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i)The stress at elastic limit.(ii) Young’s modulus.(iii) Percentage elongation. (iv)Percentage reduction in area. (v)Ultimate tensile stress.
A hot rolled steel tension test sample has a diameter of 6 mm and the original gage lenght of 30 mm. In a test to fracture, the stress and strain data below were obtained. Complete table.
Mild Steel is tested in the laboratory. The data obtained are:Length of Specimen = 320 mmDiameter of Specimen = 30 mmElongation under a load of 20 kN = 0.055 mmLoad at Yield Point = 130 kNMaximum Load = 210 kNLoad at fracture = 115 kNLength of Specimen at failure = 380 mmDiameter of Specimen at failure = 17.5 mm Calculate: (1).Young’s Modulus (2). Yield Stress (3). Ultimate Stress
A tensile test is being conducted on a steel-rod specimen with a gauge length of L0=4.0 in and an initial diameter of d0=0.75 in. If the final length of the rod at fracture is Lt= 5.53 in, find the percent elongation of the rod at fracture
The Highest load sustained druing an uniaxial tensile testing experiment is 7,500lb. If the original cross section has a diamter of 0.25in, what is the ultimate tensile strength? (please also make a drawing)
Examination of Properties of Material (parctical) ASteel bar of (25mm) diameter was tested in tension and results were recorded as Load at Yield 218.13KN,Ultimate load (278.2KN).The Elongation measured over gauge length of (100mm) was ( 12.62mm)at Fracture point and minimum diameter was (23.64mm) determine Yield stress,Ultimate stress,%Elongation, %rudection in area إضافة ملف
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
How can I solve for the %0.2 offset strain and the calculated stress? Original diameter : 6mm Original length : 30mm Fracture diameter : 4.54mm
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.
A tensile specimen havign a diameter of 6 mm and a gauge length of 50 mm was tested to fracture and the stress-strain diagram is show. Poisson's ratio of material, v = 0.3 Determine the load P that the sample is subjected to when a stress of 300 MPa is applied. What is the instantaneous diameter of the sample given a longitudinal strain of 0.002?
A Brass specimen is subjected to a Tensile test in a laboratory. The following data obtained are: Length of Specimen = 367 mm; Diameter of Specimen = 19 mm; Yield Stress = 124 N/mm?: Ultimate Stress = 217 N/mm?: Fracture Stress = 183 N/mm?: % of Elongation = 50 % % of Reduction in area = 27 %. Determine the elongation at 103 kN, Load at yielding. Maximum load, Load at fracture, Final Length & Final diameter. Take Young's Modulus as 104 GPa.