Textbook Question
Chapter 10, Problem 10.11P
Test results of a steel specimen indicated an ultimate tensile strength of 827 MPa and a yield stress of 350 MPa. If the tensile allowable stress per design specifications is 210 MPa, compute the factor of safety based on
a. yield stress
b. tensile strength
Expert Solution & Answer
Learn your wayIncludes step-by-step video
schedule04:29
Students have asked these similar questions
The proof stress of a material under tensile loading can be considered as
can be considered as equivalent to the ultimate tensile strength for aluminium alloys
being only applied to engineering steels during a tensile test
the intercept on the stress stain curve for a given strain where a line draw is parallel to the
elastic response line.
the stress at yield for materials have no defined yield stress
In a standard tensile test a steel rod of 7/8 in. in diameter is subjected to a tension force of 17 kips. Determine the ratio of the shear modulus to the modulus of elasticity of a material whose Poisson's ratio is 0.25.
1. Define the terms load , stress and strain. Discuss the various types of stresses and strain.
2. What is the difference between modulus of elasticity and modulus of rigidity?
3. Explain clearly the bearing stress developed at the area of contact between two members.
4.
What useful informations are obtained from the tensile test of a ductile material?
5. What do you mean by factor of safety?
6. List the important factors that influence the magnitude of factor of safety.
What is meant by working stress and how it is calculated from the ultimate stress or yield stress of a
material? What will be the factor of safety in each case for different types of loading?
8. Describe the procedure for finding out the stresses in a composite bar.
7.
9. Explain the difference between linear and lateral strain.
10.
Define the following:
(a) Poisson's ratio,
(b) Volumetric strain, and
(c) Bulk modulus
11.
Derive an expression for the impact stress induced due to a falling load.
12.
Write short notes on…
Chapter 10 Solutions
Applied Statics and Strength of Materials (6th Edition)
Ch. 10 - A 916 - in. - diameter steel rod is tested in...Ch. 10 - A concrete cylinder 150 mm in diameter was tested...Ch. 10 - Prob. 10.3PCh. 10 - The data from the tension test of a steel specimen...Ch. 10 - An 18-in.-long titanium alloy rod is subjected to...Ch. 10 - ASTM A36 steel rods are used to support a balcony....Ch. 10 - A 450-mm-long AISI 1020 steel rod is subjected to...Ch. 10 - A tension member in a roof truss is composed of...Ch. 10 - A short, solid, compression member of circular...Ch. 10 - A main cable in a large bridge is designed for a...
Ch. 10 - Test results of a steel specimen indicated an...Ch. 10 - A concrete canoe in storage is supported by two...Ch. 10 - A load is applied to a rigid bar that is...Ch. 10 - Prob. 10.14CPCh. 10 - Write a program that will allow a user to input...Ch. 10 - A 12 - in. - diaiíct.cr structural nickel steel...Ch. 10 - Compute the modulus of elasticity of a copper...Ch. 10 - A concrete cylinder 6 in. in diameter was tested...Ch. 10 - An aluminum bar 2 in. by 12 - in. in cross section...Ch. 10 - During a tensile test of a steel specimen, the...Ch. 10 - A 12.5-mm-diameter steel rod was subjected to a...Ch. 10 - Prob. 10.22SPCh. 10 - A standard steel specimen having a diameter of...Ch. 10 - 10.24 A tension member in a structure is composed...Ch. 10 - A pair of wire cutters is designed to operate...Ch. 10 - Calculate the end bearing length required for a...Ch. 10 - Design a 3-m-long rod subjected to a tensile load...Ch. 10 - The collar bearing shown is subjected to a...Ch. 10 - A 10-ft-long steel member is subjected to a...Ch. 10 - Two steel bars A and B support a load P, as shown....Ch. 10 - Prob. 10.31SP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
1.1 What is the difference between an atom and a molecule? A molecule and a crystal?
Manufacturing Engineering & Technology
In each case, determine the internal normal force between lettered points on the bar. Draw all necessary free-b...
Statics and Mechanics of Materials (5th Edition)
The force in each member of truss and the state of members are in Tension or Compression.
Engineering Mechanics: Statics & Dynamics (14th Edition)
What parts are included in the vehicle chassis?
Automotive Technology: Principles, Diagnosis, And Service (6th Edition) (halderman Automotive Series)
Determine the equations of the elastic curve using the coordinates x1 and x3. What is the slope at B and deflec...
Mechanics of Materials (10th Edition)
A brass weight is to be attached to the bottom of the cylinder described in Problems 5.22 and 5.23 so that the ...
Applied Fluid Mechanics (7th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Assume suitable value for any missing data. Two cylindrical parts are to be assembled to make an interference fit. The nominal diameter of the assembly is 100 mm. Before assembly, the inner member (copper) has an outer radius that is 0.2 mm larger than the inner radius of the outer member (aluminum). If there is no other force acting on the assembly, determine the maximum and minimum principal stress in both the members. Assume Poisson's ratio of 0.3 for both the materials. Also take rj = 30 mm for copper cylinder and ro = 80 mm for aluminum cylinder.arrow_forwardyields under a load of 8KN; it attains a max load of 15KN and breaks finally A tensile test is carried out on a bar of mild steel of diameter 20mm. The bar Еxample at a load of 7KN. Estimate yP (i) The tensile stress at the yield point (ii) The ultimate tensile test ii. Max loa (iii) The average stress at the breaking point if the diameter of neck is Omm.arrow_forwardWith aid of diagram, describe a tensile experiment. Include the stress-strain curvearrow_forward
- You are in charge of designing a new fixture for a “universal testing machine” that will attach a tensile specimen to the machine using a clevis—a U-shaped piece with holes drilled through the two arms—and a cylindrical pin that passes through the clevis and the specimen. If the maximum load exerted by the machine is 30 kN and the pin is to be made of some sort of steel, what is the minimum pin diameter needed to ensure that the shear stress in the pin does not exceed 600 MPa? Assume that the steel has similar elastic properties to pure Fe.arrow_forwardProblems 2. Mild Steel is tested in the laboratory. The data obtained are: Length of Specimen = 320 mm / Diameter of Specimen = 30 mm / Elongation under a load of 20 kN = 0.055 mm Load at Yield Point = 130 kN Maximum Load = 210 kN Load at fracture = 115 kN Length of Specimen at failure = 380 mm Diameter of Specimen at failure = 17.5 mm Calculate (1).Young's Modulus (2). Yield Stress (3). Ultimate Stress (4). Fracture Stress (5). % Elongation (6). % Reduction in Area.arrow_forwardA cylindrical specimen of 1018 steel having a diameter of 6.35 mm and a gauge length of38.1 mm is pulled in tension. Use the load-elongation characteristics tabulated below. Determine the tensile strength of this alloy.arrow_forward
- 1. Plot the engineering stress & strain diagram of an alloy having a tensile test result found in Table 1. The tensile test specimen has a diameter of 12.5mm and a gage length of 50.0mm. The given alloy is used to make a 30.0mm diameter cylinder, which is placed inside a hardened circular steel casement with a 30.01mm inner diameter. Table 1: Tensile test results of an alloy Change In Length (mm) Change In Diameter (mm) Load (kN) 0.000 0.0000 0.0000 4.364 0.0254 0.0019 -0.0057 13.092 0.0762 21.819 0.1270 0.0095 30.547 32.729 0.1778 0.7620 34.911 3.0480 30.01 mm O F Rigid Plate Cylindrical Alloy -Steel casement Figure k Section view of the steel casement encapsulating the cylindrical alloy 2. Determine the required minimum value of F such that the cylindrical alloy would touch the walls of the steel casement.arrow_forwardA tensile-testing apparatus is to be constructed that must withstand a maximum load of 293516 N. The design calls for two cylindrical support posts, each of which is to support half of the maximum load; the minimum yield and tensile strengths of this alloy are 343 MPa and 565 MPa or 82,000 psi respectively.what is required diameter? Take factor of safety is 2.3arrow_forwardStress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…arrow_forward
- a)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?arrow_forwardThe % of error between a theoretical shear modulus of 65 GPa and an experimental modulus of rigidity of 60235 MPa is: Select one: O a. 0.0791 % O b. 7.33 % O c. 0.0668 % O d. 7.9 % Torrion test is annlied to study the properties of a material subjected to tensile force.arrow_forwardA copper tube with wall thickness of 8 mm must carry an axial tensile force of 175 kN. The allowable tensile stress is 90 MPa. The minimum required inside diameter is approximately: Match each item to a choice: di Choices: # 70 mm :80 mm :85 mm #65 mm :75 mm : 90 mmarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
EVERYTHING on Axial Loading Normal Stress in 10 MINUTES - Mechanics of Materials; Author: Less Boring Lectures;https://www.youtube.com/watch?v=jQ-fNqZWrNg;License: Standard YouTube License, CC-BY