Concept explainers
The time required for the pit to corrode through the wall.
Answer to Problem 58AAP
The time required for the pit to corrode through the wall is
Explanation of Solution
Write the expression for corrosion rate.
Here, the corrosion rate is
The current density is expressed as,
Substitute
Conclusion:
It is assumed that the pit is in the shape of cylinder.
The density of the aluminum is
The mass of the cylindrical aluminum pit
The top surface area of the cylindrical pit is expressed as follows.
Refer Table 13.1, “Standard electrode potentials at 25 °C”.
The anodic reaction of aluminum is as follows:
Here, the number of electrons produced is,
Refer Figure 2.3, “Periodic Table of Elements”
The atomic mass of aluminum is,
Substitute
Thus, the time required for the pit to corrode through the wall is
Want to see more full solutions like this?
Chapter 13 Solutions
Foundations of Materials Science and Engineering
- Fill in the table below? Which corrosion are seen in the figures? Briefly explain causes and preventations of these corrosions.arrow_forwardHow to measure the corrosion inhibition efficiency of a metal? And how to perform the weight loss method?arrow_forwardIdentify two metals that do not corrode easily in the presence of oxygen and water. Explain why theydo not corrode. How are these metals useful? How do the uses of these metals depend on their resistance to corrosion?arrow_forward
- Why do we analyse the rate of corrosion?arrow_forwardIn preventing corrosion of iron, a stronger reducing agent called sacrificial anode such as zinc is used to coat iron. Select one: True Falsearrow_forward1. (A) The heat treatment of a material (lets say "steel") will affect it corrosion performance? why/why not?. (B) A pice of Zn metal is exposed to three different environments as shown below. Which case will have the highest corrosion rate and why? 山山山 Zn Zn Zn HCL HCL + Oxygen HCL Onygen Fe (C) Ddifference betweenActive and passive material/metals?arrow_forward
- For the following pairs of alloys that are coupled in seawater, predict the possibility of corrosion; if corrosion is probable, note which metal/alloy will corrode. (a) Aluminum and cast iron (b) Inconel and nickel (c) Cadmium and zinc (d) Brass and titanium (e) Low-carbon steel and copperarrow_forwardFor the alloy of Brass and Titanium that are coupled in seawater, predict the possibility of corrosion; if corrosion is probable, note which metal/alloy will corrode. Answer:arrow_forward(a) What is the most likely form of corrosion for nuts and bolts in a galvanized steel plate shown in Figure 3.1. Figure 3.1 (b) What is the chemical cause of this type of corrosion? (c) Which non-destructive testing (NDT) technique(s) will you implement to evaluate the presence/severity of such damage and what repair would you perform on this plate? Why? (d) What design controls will you recommend to minimize this type of corrosion in future parts?arrow_forward
- Discuss intergranular corrosion and give examples for each type.arrow_forwardWhat are the most effective corrosion control methods used in mechanical engineering applications, and how do they prevent or mitigate corrosion?arrow_forwardWhat are the various types of corrosion encountered in mechanical engineering, and how do they differ in terms of their mechanisms and effects on materials?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY