Degarmo's Materials And Processes In Manufacturing
13th Edition
ISBN: 9781119492825
Author: Black, J. Temple, Kohser, Ronald A., Author.
Publisher: Wiley,
expand_more
expand_more
format_list_bulleted
Concept explainers
Textbook Question
Chapter 13, Problem 5P
Figure 13.Ashows the wall profile of a cast iron coupling and the shrinkage porosity that was observed in the cast product. If the interior profile must be maintained, suggest possible changes to the design that would enable the casting of a defect-free product.
FIGURE 13.A
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
What are the materials that can be produced by the shell casting method and how are they produced?
Manufacturing Processes
How to perform the sand casting of hollow piece and how to verify the calculated solidification time?
Q1/ In a homogeneous solidification process, assume molten metal solidifies into a spherical
nucleus with a BCC structure. The given data are; lattice parameter (0.292 nm), the heat of
fusion energy (1.85×10-9 J/m³), latent surface free energy (0.204 J/m²), critical radius (1-35
nm), equilibrium melting temperature (1516 K), and room temperature (27 °C). Calculate the
following for this metal;
(a) supercooling value temperature (b) activation tree energy (c) number of atoms in a
nucleus of critical size.
Chapter 13 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 13 - What are the six activities that are conducted on...Ch. 13 - What is materials processing?Ch. 13 - What are the five basic families of...Ch. 13 - Describe the capabilities of the casting process...Ch. 13 - What are some of the various mold materials and...Ch. 13 - How might the desired production quantity...Ch. 13 - Why is it important to provide a means of venting...Ch. 13 - What types of problem or defect can occur if the...Ch. 13 - Why might product removal be less of a problem...Ch. 13 - What is a casting pattern? Flask? Core? Mold...
Ch. 13 - In a horizontally parted two-part mold, what is...Ch. 13 - What are some of the components that combine to...Ch. 13 - What is a parting line or parting surface?Ch. 13 - What is draft, and why is it used?Ch. 13 - Why is it important to control the solidification...Ch. 13 - What are the two stages of solidification, and...Ch. 13 - Why is it that most solidification does not begin...Ch. 13 - Why might it be desirable to promote nucleation in...Ch. 13 - Nucleation generally begins at preferred sites...Ch. 13 - Why might directional solidification be desirable...Ch. 13 - Describe some of the key features observed in the...Ch. 13 - What is superheat?Ch. 13 - Prob. 23RQCh. 13 - What is a liquidus temperature? A solidus...Ch. 13 - What is the freezing range for a metal or alloy?Ch. 13 - Discuss the roles of casting volume and surface...Ch. 13 - What characteristics of a specific casting process...Ch. 13 - What is the correlation between cooling rate and...Ch. 13 - What is the chill zone of a casting, and why does...Ch. 13 - Which of the three regions of a cast structure is...Ch. 13 - What is dross or slag, and how can it be prevented...Ch. 13 - What are some of the possible approaches that can...Ch. 13 - What is a misrun or cold shut, and what causes...Ch. 13 - What is fluidity, and how can it be measured?Ch. 13 - What is the most important factor controlling the...Ch. 13 - What defect can form in sand castings if the...Ch. 13 - Why is it important to design the geometry of the...Ch. 13 - Why might it be preferable to attach gates to the...Ch. 13 - Prob. 39RQCh. 13 - What are some desirable features in the sprue...Ch. 13 - What is a choke, and how does its placement affect...Ch. 13 - What features can be incorporated into the gating...Ch. 13 - What are some of the materials and designs of...Ch. 13 - What factors might influence the positioning of...Ch. 13 - What features of the metal being cast tend to...Ch. 13 - What are the three stages of contraction or...Ch. 13 - Why is it more difficult to prevent shrinkage...Ch. 13 - What steps can be taken to compensate for the...Ch. 13 - During what stage of shrinkage might hot tears...Ch. 13 - What is the role of a riser?Ch. 13 - Why is it desirable to design a casting to have...Ch. 13 - What is yield, and how does it relate to the...Ch. 13 - Based on Chvorinovs rule, what would be an ideal...Ch. 13 - Define the following riser-related terms: top...Ch. 13 - What assumptions were made when using Chvorinovs...Ch. 13 - Discuss aspects relating to the connection between...Ch. 13 - What is the purpose of a chill? Of an insulating...Ch. 13 - What are some materials that are commonly used to...Ch. 13 - What types of modifications or allowances are...Ch. 13 - Prob. 60RQCh. 13 - What is the purpose of a draft or taper on pattern...Ch. 13 - Why is it desirable to make the pattern allowances...Ch. 13 - What additional adjustment or correction must be...Ch. 13 - What are some of the features of the casting...Ch. 13 - Prob. 65RQCh. 13 - What are some design recommendations for inside...Ch. 13 - What are some appearance considerations in parting...Ch. 13 - Prob. 68RQCh. 13 - Prob. 69RQCh. 13 - Using Chvorinovs rule as presented in the text...Ch. 13 - Reposition the riser in Problem 1 so that it sits...Ch. 13 - A rectangular casting having the dimensions 3 in....Ch. 13 - A cylinder with a diameter of 2.5 in. and a height...Ch. 13 - Figure 13.Ashows the wall profile of a cast iron...Ch. 13 - Investigate various experimental techniques to...Ch. 13 - Porosity within a casting can be either...Ch. 13 - The chapter text describes various materials that...Ch. 13 - What is the most likely source of the gas bubbles?...Ch. 13 - What factors may have caused the penetration...Ch. 13 - Prob. 3CSCh. 13 - Prob. 4CSCh. 13 - Prob. 5CS
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A flat plate is to be cast in an open mold whose bottom has a square shape that is 200 mm by 200 mm. The mold is 40 mm deep. A total of 106 mm3 of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.0%. The linear shrinkage due to thermal contraction after solidification is 1.3%. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its 200 mm by 200 mm dimensions until solidification is completed, determine the final dimensions of the plate.arrow_forwardQuestion 3 3.1 Briefly explain the Casting and Molding processes and define their basic requirements. 3.2 If a manufacturer was asked to produce a set of plastic bottles, which method would you suggest? Justify your answer. 3.3 What is the Forging process? Explain the process including two forged products. 3.4 Briefly explain the heat treatment processing techniques using a phase diagram.arrow_forwardThe majority of automobile alloy wheels are to be produced from A356 aluminum alloy by low pressure casting technique. Which method/s would you prefer to strengthen the wheels? Justify your answers and explain the detailed procedure steps which you would follow (Hint: You may need to check the related literature and the chemical composition of the alloy in order to determine the right job/s).arrow_forward
- What means product quality ? What characristics does the term product quality include ? 2 - what steps are included in the molding process, list them ?arrow_forward4) List the passageway (gating system) elements in sand casting moulds and show them with drawing? Draw the stress-strain curve and gives the stress and strain equations for both Engineering and True stress-strainarrow_forwardWhich of these factors causes more porosity to form toward the interior of a casting rather than toward the outside? (a) Gasses are less soluble in the solid metal than the liquid, so solidified areas push dissolved gasses toward the interior. (b) Casting under a vacuum causes gasses near the liquid metal surface to be drawn out of the liquid during solidification. (c) The feeding structures of the mold are designed to force entrapped air into the center of the casting. (d) Draft on the mold wall forces air bubbles toward the interior of the solidifying metal. (e) None of the above Non-eutectic alloys (most commercial alloys) solidify over a temperature range. Which of the following statements explains how this affects the casting process. (a) Solidified non-eutectic alloys are especially difficult to remove from metal dies (b) Non-eutectic alloys have significantly less fluidity than pure metals or eutectic alloys. (c) Non-eutectic alloys solidify starting from the outside of the…arrow_forward
- 2) Explain the reasons for shrinkage that occurs during solidification of a cylindrical casting What do you make for compensation of shrinkage depending on the casting operation?arrow_forward2b) Figure 3 shows a cooling curve of Cadmium (Cd). Determine (i) the solidification temperature;(ii) the superheat;(iii) the cooling rate, just before solidification begins; (iv) the total solidification time; (v) the local solidification time; and(vi) If the cooling curve was obtained at the center of the casting sketched in the figure, determine the mold constant, assuming that n = 2.arrow_forwardWhat is the typical industrial reduction ratio for an ingot while being processed into a forging? Group of answer choices 7:2 3:1 2:1 10:1 How are oxides removed from the melt pool during a casting process? Group of answer choices Machined after solidification Collected in slag Allowed to diffuse out into the air Vacuum degassingarrow_forward
- A flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.arrow_forwardWhen casting a 4x10x20 in. Part, which has a top overflow with a H / D = 1.5 ratio, you want to determine the height and diameter of the overflow to prevent shrinkage in the part to be cast. Note: Remember that to achieve this, the overflow has to solidify some time after the piece has solidified, since in this case the overflow acts as a riser.arrow_forward3) What are the means of elastic and plastic deformations? List the passageway (gating system) elements in sand casting moulds and show them with drawing?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license