Question
Chapter 2, Problem 2.83P
To determine
The compressive force required.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with a force of 40, 000 N. If the deformation is totally elastic, what is the strain experienced by the specimen along the lateral direction?
For some metal alloy, a true stress 345 MPa (50040 psi) produces a plastic true strain of 0.02. How much will a specimen of this material elongate when a true stress of 418 MPa (60630 psi) is applied if the original length is 500 mm (19.69in) ? Assume a value of 0.22 for the strain- hardening exponent, n
A strip of metal is originally 5 m long. It is stretched in 3 steps: first to a length of 6
m, then to 7 m and finally to 8 m. The original cross section area of the metal strip is
40 mm?. Compute the final cross section and find the percentage reduction in area
due to the above stretching process. Also calculate the force required for the final
stage of stretching, assuming that the true stress true strain relation for the
material is given as o = 700 0.48 MPa.
5 (c)
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
Ch. 2 - Prob. 2.1QCh. 2 - Prob. 2.2QCh. 2 - Prob. 2.3QCh. 2 - Prob. 2.4QCh. 2 - Prob. 2.5QCh. 2 - Prob. 2.6QCh. 2 - Prob. 2.7QCh. 2 - Prob. 2.8QCh. 2 - Prob. 2.9QCh. 2 - Prob. 2.10Q
Ch. 2 - Prob. 2.11QCh. 2 - Prob. 2.12QCh. 2 - Prob. 2.13QCh. 2 - Prob. 2.14QCh. 2 - Prob. 2.15QCh. 2 - Prob. 2.16QCh. 2 - Prob. 2.17QCh. 2 - Prob. 2.18QCh. 2 - Prob. 2.19QCh. 2 - Prob. 2.20QCh. 2 - Prob. 2.21QCh. 2 - Prob. 2.22QCh. 2 - Prob. 2.23QCh. 2 - Prob. 2.24QCh. 2 - Prob. 2.25QCh. 2 - Prob. 2.26QCh. 2 - Prob. 2.27QCh. 2 - Prob. 2.28QCh. 2 - Prob. 2.29QCh. 2 - Prob. 2.30QCh. 2 - Prob. 2.31QCh. 2 - Prob. 2.32QCh. 2 - Prob. 2.33QCh. 2 - Prob. 2.34QCh. 2 - Prob. 2.35QCh. 2 - Prob. 2.36QCh. 2 - Prob. 2.37QCh. 2 - Prob. 2.38QCh. 2 - Prob. 2.39QCh. 2 - Prob. 2.40QCh. 2 - Prob. 2.41QCh. 2 - Prob. 2.42QCh. 2 - Prob. 2.43QCh. 2 - Prob. 2.44QCh. 2 - Prob. 2.45QCh. 2 - Prob. 2.46QCh. 2 - Prob. 2.47QCh. 2 - Prob. 2.48QCh. 2 - Prob. 2.49PCh. 2 - Prob. 2.50PCh. 2 - Prob. 2.51PCh. 2 - Prob. 2.52PCh. 2 - Prob. 2.53PCh. 2 - Prob. 2.54PCh. 2 - Prob. 2.55PCh. 2 - Prob. 2.56PCh. 2 - Prob. 2.57PCh. 2 - Prob. 2.58PCh. 2 - Prob. 2.59PCh. 2 - Prob. 2.60PCh. 2 - Prob. 2.61PCh. 2 - Prob. 2.62PCh. 2 - Prob. 2.63PCh. 2 - Prob. 2.64PCh. 2 - Prob. 2.65PCh. 2 - Prob. 2.66PCh. 2 - Prob. 2.67PCh. 2 - Prob. 2.68PCh. 2 - Prob. 2.69PCh. 2 - Prob. 2.70PCh. 2 - Prob. 2.71PCh. 2 - Prob. 2.72PCh. 2 - Prob. 2.73PCh. 2 - Prob. 2.74PCh. 2 - Prob. 2.75PCh. 2 - Prob. 2.76PCh. 2 - Prob. 2.78PCh. 2 - Prob. 2.79PCh. 2 - Prob. 2.80PCh. 2 - Prob. 2.81PCh. 2 - Prob. 2.82PCh. 2 - Prob. 2.83PCh. 2 - Prob. 2.84PCh. 2 - Prob. 2.85PCh. 2 - Prob. 2.86PCh. 2 - Prob. 2.87PCh. 2 - Prob. 2.88PCh. 2 - Prob. 2.89PCh. 2 - Prob. 2.90PCh. 2 - Prob. 2.91PCh. 2 - Prob. 2.92PCh. 2 - Prob. 2.93PCh. 2 - Prob. 2.94PCh. 2 - Prob. 2.95PCh. 2 - Prob. 2.96PCh. 2 - Prob. 2.97PCh. 2 - Prob. 2.98PCh. 2 - Prob. 2.99PCh. 2 - Prob. 2.100PCh. 2 - Prob. 2.101P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with a force of 40, 000 N. If the deformation is totally elastic, what is the strain experienced by the specimen along the longitudinal direction?arrow_forwardtensile test is performed to determine the parameters strength constant C and strainrate sensitivity exponent m for a certain metal. The temperature at which the test is performed = 500°C. At a strain rate = 10/s, the stress is measured at 140 MPa; and at a strain rate = 150/s, the stress = 280 MPa. (a) Determine C and m. (b) If the temperature were 600°C, what changes would you expect in the values of C and m?arrow_forwardThe strength coefficient and strain-hardening exponent of a certain test metal are 750 MPa and 0.25, respectively. A cylindrical specimen of the metal with starting diameter = 75 mm is stretched. If the average flow stress on the part is 450 MPa determine the final diameter of the specimen.arrow_forward
- In True stress-true-strain curve in tension of solid metal cylinder 45 mm high and 8 mm in diameter, two pairs of values of stress and strain were given for the specimen metal after it had yielded (1) true stress = 217 MPa, and true strain = 0.35; and (2) true stress = 259 MPa, and true strain = 0.68. Based on these data points, determine the following: a) The average flow stress that the metal experiences if it is subjected to a stress that is equal to its strength coefficient K. b) The work done that the metal experiences if it is subjected to elongation in height of 45% c) If during the deformation the relative speed = 20 mm/s, determine the strain rate at h = 50 mm and h = 70 mm.arrow_forwardA cylindrical specimen of brass that has a diameter of 15 mm, a tensile modulus of 120 GPa, and a Poisson’s ratio of 0.30 is pulled in tension with force of 50,000 N. If the deformation is totally elastic, what is the approximate strain experienced by the specimen?arrow_forwardA ductile specimen that has an initial length of 10 cm is tested under uniaxial loading. If the test is under tension and the nominal strain is 21.9%, please calculate the true strain in %.arrow_forward
- A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile test under maximum load 66KN with elongation 7.5mm, and the yield load of this specimen is 15KN with elongation 2.4mm. Calculate: 1- The engineering ultimate stress (ultimate tensile strength), and engineering strain at this point. 2- The engineering stress and strain at yield point. 3- The modulus of elasticity, and the modulus of resilience. 4- The final or fracture strain of a steel specimen, if you know that the final length of specimen after testing is 58.5mm. 5- The true stress and strain for ultimate point. any four point sirarrow_forwardA tensile specimen of cylindrical brass cartridge subjected to a load of 350 kg has a cross section diameter of 3.5 mm and a gage length of 25 mm. Calculate the Young's modulus and engineering strain that occurred during a test if the distance between gage markings is 26.5 mm after the test.arrow_forwardThe data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracturearrow_forward
- 2. A metal alloy has been tested in a tensile test with the following results for the flow curve parameters: strength coefficient = 620.5 MPa and strain-hardening exponent 0.26. The same metal is now tested in a compression test in which the starting height of the specimen = 62.5 mm and its diameter = 25 mm. Assuming that the cross section increases uniformly, determine the load required to compress the specimen to a height of (a) 50 mm and (b) 37.5 mm. 3. The starting length of a shaft is 25.00 mm. This shaft is to be inserted into a hole in an expansion fit assembly operation. To be readily inserted, the shaft must be reduced in length by cooling. Determine the temperature to which the shaft must be reduced from room temperature (20° C) in order to reduce its length to 24.98 mm. Refer to the Table below. Volumetric properties in U.S. customary units for selected engineering materials. Coefficient of Thermal Expansion, a Density, p Ib/in Melting Point, T Material g/cm C'x 10 F'x 10 6…arrow_forwardThe data shown in the accompanying table are From a tensile test of high-strength steel. The test specimen has a diameter of 0.505 in. and a gage length of 2.00 in. (see figure for Prob. 1.5-3). At fracture, the elongation between the gage marks is 0.12 in. and the minimum diameter is 0.42 in. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (the slope of the initial part of thestress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 2.00 in., and percent reduction in area. TENSILE-TEST DATA FOR PROB. L.5-7 Laid (lb) Elongation (in) 1000 0.0002 2000 0.0006 6000 0.0019 10,000 0.0033 12,000 0.0039 12,900 0.0041 13,400 0.0047 13,600 0.0054 13,800 0.0063 14,000 0.0090 14,400 0.0102 15,200 0.0130 16,800 0.0230 18,400 0.0336 20,000 0.0507 22,400 0.1108 22,600 Fracturearrow_forwardEngineering strain of a mild steel sample is recorded as 0.100%. The true strain isarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
An Introduction to Stress and Strain; Author: The Efficient Engineer;https://www.youtube.com/watch?v=aQf6Q8t1FQE;License: Standard YouTube License, CC-BY